At Steelo Fabrica, we produce the best quality of naval brass products, including CW711R flat bars. As an integrated manufacturer, we have a comprehensive and far-reaching collection of UNS C48500 flat bars available in various lengths, sizes, and finishes to meet the client’s precise requirements.
Table of Content
What is the composition of the UNS C48500 flat bar?
The main chemical composition consisted in UNS C48500 flat bar are:
Apart from the above mentioned alloying elements, there is also zinc (Zn) present in the composition of the naval brass flat CW711R bars.
It is a copper alloy UNS C48500 that holds many beneficial properties and characteristics, making this naval brass more popular among other materials.
UNS C48500 flat bars have the property of great soldering, good for brazing. This alloy provides a high degree of machinability. Also, it has exceptional corrosion resistance quality, due to which it is highly recommended and useful for the marine industry and aqueous media applications.
The following properties and qualities predominately characterize the unparalleled quality of our naval brass flat bar:
Industries in which these naval brass CW711R flat bars are used:
We supply UNSC48500 flat bars with excellent mechanical properties that are frequently used by organizations in various industries, including:
Our company extends its services throughout numerous manufacturing industries through consistent statistical monitoring for obtaining accurate results. We provide the naval brass alloy materials in various standard shapes as well as custom cut copper alloys.
Specification : ASTM B21/ ASME SB21
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Hollow Bars : Min Bore Size 20 mm and Max OD 100 mm
Flat Bars : 6mm To 130 mm
Ingots: AS per Specification
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Flat, Patta Patti
|BD||Bright drawn||SRE||Slit rolled edge|
|CG||Centreless ground||HF||Hot finished|
|CF||Cold finished||HRAP||Hot rolled annealed and pickled|
|P&T||Peeled and turned||RT||Rough turned/peeled|
|ST||Smooth turned||PR||Peeled and reeled|
|Chemical Element||% Present|
|Copper (Cu)||61.00 – 63.00|
|Tin (Sn)||1.00 – 1.50|
|Lead (Pb)||0.20 – 0.60|
|Iron (Fe)||0.0 – 0.10|
|Nickel (Ni)||0.0 – 0.20|
|Others (Total)||0.0 – 0.20|
|Elastic (Young’s, Tensile) Modulus||Elongation at Break||Poisson’s Ratio||Shear Modulus||Shear Strength||Tensile Strength: Ultimate (UTS)||Tensile Strength: Yield (Proof)|
|100 GPa – 15 x 106 psi||17 to 34 %||0.31||40 GPa||240 to 290 MPa||370 to 480 MPa||120 to 290 MPa|
We offer a broad range of ASTM B21 Naval Brass CW711R Flat Bars through a worldwide network of stock-keeping branches. These C48500 Naval Brass Alloy Bars is use in various industries like :