Steelo Fabrica is one of the pioneer distributors, manufacture and trader of Brass Flat Bars. Our company is engaged in providing Brass UNS C83600 flat bars made out of supreme quality raw materials.
These flat bars are widely used in manufacturing industries for supporting components.
Table of Content
Chemical composition percentage that brasses UNS C83600 flat bars holds:
• Copper (83% – 86%)
• Tin (4.0% – 6%)
• Lead (4% – 6%)
• Zinc (4% – 6%)
• Antimony (0% – 0.25%)
• Aluminum (0% – 0.005%)
• Iron (0% – 0.30%)
• Nickel (0% – 1%)
• Phosphorus (0% – 0.05%)
• Silicon (0% – 0.005%)
These are the chemical composition percentage of Brass UNS C83600 material which strengthen the material properties.
Let’s discuss attributes of the Brass UNS C83600 material:
Due to elements present in the composition, the alloys group is typically found in the plumbing application sector. The most widely used alloy in this family is UNS C83600 Brass, known for its affordable cost and good machinability.
Along with the good machining properties, it also possesses great casting properties. The lead content present in the alloy ensures pressure tightness. This brass is also used for low-cost bearing materials, which came under low loads applications.
It is an alloy which not only offers good resistance against corrosion but also for corrosion against wear and impact. It has an excellent anti-friction quality, good conductivity. It has a tensile strength of 2090 kg/cm sq. and 60 – 65 of Brinell hardness.
The weldability of Brass Flat Bars can be assumed to be weld easier. These Brass flat Bars are more resistant to general pitting and crevice corrosion than the conventional alloy. This material also offers higher creep, stress rupture and tensile strength at a higher temperature.
The UNS C83600 Bronze is mainly used in:
• Water and steam valves
• Pumps parts
• Ornamental pieces
• Hydraulic Applications
• Pump drivers
• Machine parts
|BD||Bright drawn||SRE||Slit rolled edge|
|CG||Centreless ground||HF||Hot finished|
|CF||Cold finished||HRAP||Hot rolled annealed and pickled|
|P&T||Peeled and turned||RT||Rough turned/peeled|
|ST||Smooth turned||PR||Peeled and reeled|
|Tensile Strength, min||Yield Strength, at 0.5% Extension Under Load, min||Elongation, in 2 in. or 50 mm min||Brinell Hardness
(500 kg load)
We offer a broad range of ASTM B505 Brass C83600 Flat Bars through a worldwide network of stock-keeping branches. These C83600 Brass Patta / Patti is use in various industries like :